| 产品说明 |
| BC-359为一支独特为了节省能源及增加生产量所开发需经稀释的凡立水。 |
| 产品特点 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 1. 烘烤温度低(110℃)及快速烘干。 |
2.导线不易碎断。 |
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 3. 低成本—需经过稀释使用。 |
|
4. 结合力强。 |
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 5 .优异的耐化学及耐磨损性。 |
|
6.UL绝缘系统认证至CLASS H等级(180℃) |
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 7.极适合自动化作业系统。 |
|
8. 符合RULE 66的污染防治标准。 |
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 9. 优异的防潮性—即使在潮湿环境下，电介质强度不会改变。 |
|
|
|
| 产品用途 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 电气产品与电子零件，各类型线圈、马达、发电机、变压器、继电器、PC电路板等。 |
|
|
|
|
|
|
|
|
|
| 使用说明 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 1. 依产品特性决定所需要稀释的浓度。 |
|
|
|
|
|
|
|
|
|
|
| 2. 预热欲处理的产品至胶带平贴，湿气除去为止。 |
|
|
|
|
|
|
| 3. 冷却至60℃。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 4. 浸没于凡立水中，10-20分钟至气泡消失为止。 |
|
|
|
|
|
|
| 5. 将产品滴干15~20分钟。 |
|
|
|
|
|
|
|
|
|
|
|
| 6. 至于烤箱烘烤，以下为建议的烘烤温度及时间。（依产品不同做适当调整） |
| *8-10小时 @ 110℃ |
*45分钟-2小时 @150℃ |
|
|
|
|
|
|
|
|
|
|
| *2-4小时 @ 120℃ |
*30分钟-90分钟 @160℃ |
|
|
|
|
|
|
|
|
|
|
| *1-3小时 @ 135℃ |
|
|
|
|
|
|
|
|
|
|
|
|
|
| *烘烤时间为产品达到烘烤温度后完全硬化所需之时间 |
|
|
|
|
|
|
| 以下为自动化作业系统所建议处理流程： |
|
|
|
|
|
|
|
| 1. 依产品特性决定所需要稀释的浓度。 |
|
|
|
|
|
|
|
|
|
|
|
| 2. 将产品预热至100℃。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 3. 冷却至60℃。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 4. 浸没于凡立水中15秒。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 5. 滴干2-4分钟。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 6. 置于烤箱烘烤。 |
|
|
|
|
|
|
|
|
|
|
|
|
|
| 7.烘烤所需时间请参照上述之温度及时间配合表。 |
|
|
|
|
|
|
| TYPICALPROPERTIES |
|
|
|
|
|
|
|
|
|
|
|
|
| Physical |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
As Shipped |
Thinned 25%(by volume) with/T-100 |
|
|
|
|
|
|
|
|
| Appearance/Color |
Clear/Amber |
Clear/Amber |
|
|
|
|
|
|
|
| Specific Gravity @700F.，ASTM D-287 |
23-270 |
30-350 |
|
|
|
|
|
|
| Viscosity，.Dolph Cup @860F |
56-74 sec. |
19-22 sec. |
|
|
|
|
|
|
|
| Film Build，mils/side，ASTM D-115 |
2-2.5 mils |
0.25-1 mils |
|
|
|
|
|
|
|
| Thinner |
T-100 |
T-100 |
|
|
|
|
|
|
| Bake Time @ 2300F. on a Strip，ASTM D-115 |
|
|
|
|
30 min. |
30min. |
|
|
|
|
|
|
| Cure Time @ 2300F. in 20 gram test cup |
2hr. |
2 hr. |
|
|
|
|
|
|
| Corrosive Effect on Copper |
None |
None |
|
|
|
|
|
|
| Bond Strength on MW-35 Magnet Wire，lbs |
@25℃ |
28 |
|
|
|
|
|
|
| @150℃ |
3.5 |
|
|
|
|
|
|
| Electrical |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Dielectric Strength， volts/mil (dry) |
3，000 |
|
|
|
|
|
|
|
|
| Dielectric Strength， volts/mil (wet) |
3，000 |
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Chemical Resistance |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Water |
Excellent |
|
|
|
|
|
|
|
|
| Acid (10% Sulfuric Acid) |
Excellent |
|
|
|
|
|
|
|
|
| Alkali (1% Sodium Hydroxide) |
Excellent |
|
|
|
|
|
|
|
|
| Salt Water |
Excellent |
|
|
|
|
|
|
|
|
| Oil. ASTM D-115 |
Passed |
|
|
|
|
|
|
|
|
| 稀释 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 在一般程序下作业时，稀释比例大约为(52:48)(BC-359:稀释剂) |
|
|
|
|
| 但请自行依产品特性调整所需之稀释比例。 |
|
|
|
|
|
|
|
| 储存 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 储存于阴凉干燥的环境(建议18℃~24℃)，并远离日光的直接照射 |
|
| 保存期限:一年 于23℃以下温度 |